The Variation Patterns of Resin Modulus in Composite under Different Curing Process Parameters

Authors

  • Xiaojun Cui
  • Shuxian Chen
  • Qinying Kang

DOI:

https://doi.org/10.6919/ICJE.202412_10(12).0018

Keywords:

Composite Materials; Thermal Curing; Elastic Modulus; Shear Modulus.

Abstract

To investigate the effects of curing process parameters on the elastic modulus and shear modulus of resin in the composite, a finite element model for the scarf repair of curved laminated plates was established based on the thermochemical and mechanical models of composite materials, as well as the linear elastic constitutive relation. Simulation calculations were conducted for different heating and cooling rates. The variation process and development patterns of the resin's elastic modulus and shear modulus were investigated. The results indicate that the onset of the increase in resin elastic modulus and shear modulus is advanced with increasing the heating rate and the resin modulus under a heating rate of 3.5 K/min begins to change approximately 3000 seconds earlier than at a heating rate of 1.5 K/min, reducing the total curing time by about 20%. And the cooling rate has no impact on the variation patterns or the development process of the resin's elastic modulus and shear modulus.

Downloads

Download data is not yet available.

References

[1] Y. T. Wang. Analysis of Temperature Field and Thermal Stress during the Curing Process of Resin Matrix Composite Repair Patch [D]. Civil Aviation Flight University of China, 2015.P. Zhao, Q. S. Tian. Research on Thermosetting Method for Composite Material Repair Patch [J]. Journal of Civil Aviation, 2024, 8(01): 107-111.

[2] A. X. Ding, S. X. Li, A. Q. Ni, et al. A Review of Numerical Simulation on Curing Deformation and Residual Stress in Thermosetting Resin Matrix Composites [J]. Acta Materiae Compositae Sinica, 2017, 34(03): 471-485.

[3] Z. Y. Ding. Research on Bonding Repair Technology of Composite Laminated Plates for General Aviation Aircraft [D]. Civil Aviation Flight University of China, 2024.

[4] D. J. Yan. Research on the Thermosetting Process of Scarf Repair for Damage in Composite Laminated Plate Structures [D]. Civil Aviation Flight University of China, 2023.

[5] K. K. Tian, C. Li, C. X. Hu, et al. Single-Objective Optimization of Scarf Repair Structure for CFRP Laminated Plates Based on Response Surface Methodology [J]. Composite Science and Engineering, 2021, (09): 22-30.

[6] KIRCHNER H P, CONWAY J C, SEGALL A E. Effect of joint thickness and residual stresses on the properties of ceramic adhesive joints: I, finite element analysis of stresses in joints[J]. Journal of the American Ceramic Society, 2010, 70 (2): 104-109.

[7] Pitanga M Y, Cioffi M O H, Voorwald H J C, et al. Reducing repair dimension with variable scarf ang les[J]. International Journal of Adhesion and Adhesives, 2021, 104: 102752.

[8] J. Zhang, X. Cheng, J. Zhang, et al. Effect of curing condition on bonding quality of scarf-repaired comp osite laminates[J]. Chinese Journal of Aeronautics, 2020, 33(08): 2257-2267.

[9] P. Zhao, Q. S. Tian. Research on Thermosetting Method for Composite Material Repair Patch [J]. Journal of Civil Aviation, 2024, 8(01): 107-111.

[10] A. Ding, S. Li, J. Wang, et al, Prediction of process-induced distortions in L-shaped composite profiles using path-dependent constitutive law[J].Applied Composite Materials,2016,23(5):1027~1045.

[11] Tavakol B, Roozbehjavan P, Ahmed A, et al. Prediction of residual stresses and distortion in carbon fiber-epoxy composite parts due to curing process using finite element analysis[J]. Journal of applied Polymer,2013,128(2):941~950.

[12] W. Tian , R. Li , Z. Zhang , et al. Curing parameters development and long-term performance of ohmic heating cured conductive cementitious composites: A comparative study on fiber fraction[J].Journal of Building Engineering,2024,91109566-.

[13] Q. S. Tian, Q. R. Tang, Y. T. Wang, et al. Analysis of Curing Temperature Field and Thermal Stress of Composite Repair Patch under Different Cooling Rates [J]. Bulletin of the Chinese Ceramic Society, 2015, 34(S1): 181-185.

[14] Z. Liu. Numerical Simulation Analysis of Curing Deformation in Thermosetting Resin Matrix Composites [D]. Harbin Institute of Technology, 2014.

[15] X. X. WANG, O. L. WANG, L. L. GAO, et al. Effects of key thermophysical properties on the curing uniformity of carbon fiber reinforcedresin composites[J]. E Polymers,2018,18:1-9.

[16] F. L. Li, Z. F. Yang, Y. Q. Cheng, et al. Research on the Curing Kinetics and Dynamic Mechanical Properties of Epoxy Resin for Fast Pultrusion [J]. China Plastics, 2023, 37(06): 66-73.

Downloads

Published

2024-11-19

Issue

Section

Articles

How to Cite

Cui, Xiaojun, Shuxian Chen, and Qinying Kang. 2024. “The Variation Patterns of Resin Modulus in Composite under Different Curing Process Parameters”. International Core Journal of Engineering 10 (12): 145-52. https://doi.org/10.6919/ICJE.202412_10(12).0018.